13
Pipeliner
www.lincolnelectric.com
Optimum performance on vertical
down hot, fill and cap passes on
s
tandard cross-country pipelines
and arctic grade pipe. Excellent
crack resistance, CTOD, and Charpy
V-Notch properties. Recommended for
API Pipe Grades X42 through X70.
WELDING POSITIONS
ADVANTAGE LINCOLN
• Produces quality welds in moderate
wind conditions with no tenting.
• Our quality driven manufacturing
system – certified to ISO 9001 –
and our exceptionally high grade raw
materials mean every coil of
Innershield delivers great arc
PIPELINER NR-207+ AWS: E71T8-K6 Self-Shielded Flux-Cored (FCAW-S) Wire Electrode
CONFORMANCE
AWS A5.29-98: E71T8-K6
ASME SFA-5.29: E71T8-K6
characteristics and superior
feedability.
•
Manufactured to actual lot control.
Actual certificates of conformance
are available upon request.
TYPICAL APPLICATIONS
• Standard cross country pipelines.
• Arctic grade pipe.
• Use these wires instead of stick for
improved productivity on pipeline
projects.
DIAMETERS / PACKAGING
MECHANICAL PROPERTIES
- As Required per AWS A5.29-98
%C %Mn %P %S %Si %Al %Ni %Cr %Mo %V
Requirements
AWS E71T8-K6
.15 .50- .03 .03 .80 1.80 .40- .20 .15 .05
max. 1.50 max. max. max. max. 1.00 max. max. max.
Typical Results .06 1.21 .007 <.003 .25 .96 .82 .03 .02 <.01
DEPOSIT COMPOSITION
- As Required per AWS A5.29-98
Diameter 14 Lb. (6.3 kg) Coil
in. (mm) [ 56 Lb. (25.4 kg)
Master Sealed Pail ]
5/64 (2.0) ED030924
NOTE: Pipeliner elec-
trodes are manufactured
under lot control. A
Certificate of Test show-
ing actual deposit chem-
istry and mechanical
properties per AWS
A5.29 is available on
request from the factory
for every lot of electrode.
(Fax 216-383-8386).
(1)
The strength and elongation properties reported were obtained from a .505” tensile specimen artificially aged at 220°F
(104°C) for 48 hours, as permitted by AWS A5.29-98. A naturally aged tensile specimen may take months to achieve the
specified properties. The time required for the natural aging of weld deposits is dependent upon ambient conditions, weld-
ment geometry, the metallurgical structure of the weld deposit and other factors.
Charpy V-Notch
Yield Strength Tensile Strength
(1)
Elongation
(1)
ft•lbf (Joules) Hardness
psi (MPa) psi (MPa) (%) @ -20°F (-29°C) @-40°F (-40°C) Rockwell B
Requirements 58,000 (400) 70,000 - 90,000 20 20 (27) Not . Not
AWS E71T-K6 min. (483 - 620) min. min. Required Required
Typical Results 58,000 - 64,000 75,000 - 80,000 20 - 33 103 - 116 109
.
84 - 90
(400 - 441) (517 - 551) (176 - 230) (147) ..
TYPICAL OPERATING
PROCEDURES
Diameter
Parameters 5/64 in. (2.0 mm)
Polarity DC-
CTWD
(1)
– in (mm) 3/4 (19)
Wire Weight – lbs/in (g/m) 1.04/1000 (18.57)
Wire Feed Speed – in/min (m/min) 70-130 (1.7-3.3)
Arc Voltage (volts) 18-21
Approx. Current (amps) 210-305
Melt-off Rate – lbs/hr (kg/hr) 4.3-8.1 (2.0-3.7)
Deposition Rate – lbs/hr (kg/hr) 3.6-6.7 (1.6-3.0)
(1)
CTWD (Contact Tip to Work
Distance). Subtract 1/4" to
calculate Electrical Stickout.